| Produced from
high-tenacity polyester fiber for the seven braided strength
cores and braided chafe protection cover. It offers high
strength with an excellent deep water mooring profile and higher
shock mitigation than HMPE fiber ropes. Because of its strength
and built-in wear protection, P-7 enables smaller diameters to
be used to minimize weight. |
|
|
- High Strength
- Excellent wear resistance
- High shock mitigation
- Low stretch at maximum strength
|
- Flexibility with firm cross section
- Lightweight
- Non-rotational
- Class I Product Specific
|
|
|
|
|
|
|
|
| • Specific
Gravity... |
| 1.38 |
|
| • Elastic
Elongation... |
| At % break strength
|
| 10% |
20% |
30% |
| 0.96% |
1.84% |
2.82% |
Rope stabilized from 200D2. Ropes cycled 50 times at each
percent of average break strength. |
|
|
|
| INCH |
MM |
LBS/100 FT |
KG/100M |
SAMSON AVERAGE STRENGTH LBS |
SAMSON AVG STRENGTH KG |
SAMSON MIN STRENGTH LBS |
SAMSON MIN STRENGTH KG |
| 1-1/2 |
36 |
73.6 |
110 |
101,000 |
45,800 |
90,900 |
41,200 |
| 1-5/8 |
40 |
85.8 |
128 |
117,000 |
53,100 |
105,000 |
47,800 |
| 1-3/4 |
44 |
98.8 |
147 |
137,000 |
62,100 |
123,000 |
55,900 |
| 1-7/8 |
46 |
113 |
168 |
156,000 |
70,800 |
140,000 |
63,700 |
| 2 |
48 |
127 |
189 |
168,000 |
76,200 |
151,000 |
68,600 |
| 2-1/8 |
52 |
143 |
213 |
201,000 |
91,200 |
181,000 |
82,100 |
| 2-1/4 |
56 |
159 |
237 |
226,000 |
103,000 |
203,000 |
92,300 |
| 2-3/8 |
57 |
177 |
263 |
252,000 |
114,000 |
227,000 |
103,000 |
| 2-1/2 |
60 |
195 |
290 |
279,000 |
127,000 |
251,000 |
114,000 |
| 2-5/8 |
64 |
214 |
318 |
307,000 |
139,000 |
276,000 |
125,000 |
| 2-3/4 |
68 |
234 |
347 |
335,000 |
152,000 |
302,000 |
137,000 |
| 2-7/8 |
69 |
254 |
378 |
363,000 |
165,000 |
327,000 |
148,000 |
| 3 |
72 |
276 |
410 |
398,000 |
181,000 |
358,000 |
162,000 |
|
|